Sub-micron sized crystalline particles of Eu3+ and Er3+-doped zirconia (ZrO2) were prepared via a wet chemical sol–gel route and post synthesis annealing. The doping was achieved by introduction of the respective rare earth salts into the zirconia precursor solution, with insitu generation of sodium chloride for stabilization of the particle surface during growth. A series of materials with differing europium content, nominally 0.3, 3 and 6 mol% within the ZrO2 lattice, were prepared for respective comparison and characterization of their optical properties following annealing at 700 °C. Average emission lifetimes of up to 2.3 ms were observed for the Eu3+-doped particles. Particle sizes, approximated from SEM micrographs, were observed in the range 250–400 nm. The synthesis of Er3+-doped ZrO2 particles (0.5 mol%) produced 300 nm sized particles which exhibited emission in the visible and infrared regions after annealing at 1000 °C. X-ray diffraction (XRD) with Rietveld analysis for phase quantification, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and photoluminescence (PL) spectra were used to characterize the samples.

Synthesis and optical properties of sub-micron sized rare earth-doped zirconia particles

FRERIS, Isidora;RIELLO, Pietro;F. Enrichi;CRISTOFORI, Davide;BENEDETTI, Alvise
2011-01-01

Abstract

Sub-micron sized crystalline particles of Eu3+ and Er3+-doped zirconia (ZrO2) were prepared via a wet chemical sol–gel route and post synthesis annealing. The doping was achieved by introduction of the respective rare earth salts into the zirconia precursor solution, with insitu generation of sodium chloride for stabilization of the particle surface during growth. A series of materials with differing europium content, nominally 0.3, 3 and 6 mol% within the ZrO2 lattice, were prepared for respective comparison and characterization of their optical properties following annealing at 700 °C. Average emission lifetimes of up to 2.3 ms were observed for the Eu3+-doped particles. Particle sizes, approximated from SEM micrographs, were observed in the range 250–400 nm. The synthesis of Er3+-doped ZrO2 particles (0.5 mol%) produced 300 nm sized particles which exhibited emission in the visible and infrared regions after annealing at 1000 °C. X-ray diffraction (XRD) with Rietveld analysis for phase quantification, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and photoluminescence (PL) spectra were used to characterize the samples.
2011
33
File in questo prodotto:
File Dimensione Formato  
OptMat1.pdf

non disponibili

Tipologia: Documento in Post-print
Licenza: Accesso chiuso-personale
Dimensione 870.86 kB
Formato Adobe PDF
870.86 kB Adobe PDF   Visualizza/Apri

I documenti in ARCA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10278/29944
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 48
  • ???jsp.display-item.citation.isi??? 48
social impact