Thin films of FeSe0.92 and FeSe0.5Te0.5 iron chalcogenide superconductors and solid solutions containing these components in different ratios have been grown on the surface of LaAlO 3 (10 bar 12) crystals by pulsed laser deposition. Films of solid solutions have been deposited by simultaneous laser ablation from two targets of the FeSe0.92 and FeSe0.5Te0.5 stoichiometric compositions onto one substrate. An X-ray diffraction study of the film structure shows that the films grown are epitaxial and their lattice parameters regularly vary with the ratio of the deposited components, which was controllably varied by changing the ablation intensities from the targets. © 2013 Pleiades Publishing, Ltd.
Investigation into the growth and structure of thin-film solid solutions of iron-based superconductors in the FeSe0.92-FeSe0.5Te0.5 system
Arpaia R.;
2013-01-01
Abstract
Thin films of FeSe0.92 and FeSe0.5Te0.5 iron chalcogenide superconductors and solid solutions containing these components in different ratios have been grown on the surface of LaAlO 3 (10 bar 12) crystals by pulsed laser deposition. Films of solid solutions have been deposited by simultaneous laser ablation from two targets of the FeSe0.92 and FeSe0.5Te0.5 stoichiometric compositions onto one substrate. An X-ray diffraction study of the film structure shows that the films grown are epitaxial and their lattice parameters regularly vary with the ratio of the deposited components, which was controllably varied by changing the ablation intensities from the targets. © 2013 Pleiades Publishing, Ltd.File | Dimensione | Formato | |
---|---|---|---|
S1063774513030243.pdf
non disponibili
Tipologia:
Versione dell'editore
Licenza:
Copyright dell'editore
Dimensione
316.44 kB
Formato
Adobe PDF
|
316.44 kB | Adobe PDF | Visualizza/Apri |
I documenti in ARCA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.