Lanthanum aluminate(LaAlO3) nanophosphors doped with erbium were successfully synthesized by a combustion process. The powders were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy(TEM) and fluorescence spectroscopy. Pure LaAlO3 phase was obtained at 800 C heated for 4h, with an average crystal size, as determined by TEM, of 60nm. Infrared emission spectra and decay times of main luminescence transitions were measured at room temperature. A strong emissionis reported at 1550nm from the (4I13=2-4I15=2) transition, which intensity depends on the Er concentration.

Combustion synthesis and spectroscopic charaterisation of LaAlO3 nanophosphors doped Er3+ ions

BENEDETTI, Alvise;F. Enrichi;
2013-01-01

Abstract

Lanthanum aluminate(LaAlO3) nanophosphors doped with erbium were successfully synthesized by a combustion process. The powders were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy(TEM) and fluorescence spectroscopy. Pure LaAlO3 phase was obtained at 800 C heated for 4h, with an average crystal size, as determined by TEM, of 60nm. Infrared emission spectra and decay times of main luminescence transitions were measured at room temperature. A strong emissionis reported at 1550nm from the (4I13=2-4I15=2) transition, which intensity depends on the Er concentration.
File in questo prodotto:
File Dimensione Formato  
CeramicsIntl12013.pdf

non disponibili

Tipologia: Documento in Post-print
Licenza: Accesso chiuso-personale
Dimensione 1.28 MB
Formato Adobe PDF
1.28 MB Adobe PDF   Visualizza/Apri

I documenti in ARCA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10278/37929
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 6
  • ???jsp.display-item.citation.isi??? 6
social impact