In this work, crosslinked hydrocarbon-based cation exchange membranes have been developed for vanadium redox flow battery applications. By Friedel-Crafts alkylation of sulfonated poly(phenylene sulfide sulfone) (sPSS), membranes with various degrees of crosslinking have been prepared in one step. Among those, the membrane containing 9% of crosslinker (sPSScl9) represents the best solution. Owing to a much higher selectivity, battery self-discharge and capacity fading (tested over 100 charge/discharge cycles at 120 mA cm−2) of sPSScl9 outperform benchmark Nafion of comparable thickness (N212). Furthermore, the crosslinking strategy permits to obtain stable membranes even in highly oxidizing environments, due to a combination of crosslinking, that holds together the polymer chains, and oxidation of sulfides to sulfones that increases the rigidity of the backbone. As a result, sPSScl9 incubated in the presence of V(V) shows unchanged ion exchange capacity and proton conductivity, and a 10× reduction of vanadium permeability with respect to untreated membranes.

Crosslinked sulfonated poly(phenylene sulfide sulfone) membranes for vanadium redox flow batteries

Gigli M.
;
Licoccia S.;
2021-01-01

Abstract

In this work, crosslinked hydrocarbon-based cation exchange membranes have been developed for vanadium redox flow battery applications. By Friedel-Crafts alkylation of sulfonated poly(phenylene sulfide sulfone) (sPSS), membranes with various degrees of crosslinking have been prepared in one step. Among those, the membrane containing 9% of crosslinker (sPSScl9) represents the best solution. Owing to a much higher selectivity, battery self-discharge and capacity fading (tested over 100 charge/discharge cycles at 120 mA cm−2) of sPSScl9 outperform benchmark Nafion of comparable thickness (N212). Furthermore, the crosslinking strategy permits to obtain stable membranes even in highly oxidizing environments, due to a combination of crosslinking, that holds together the polymer chains, and oxidation of sulfides to sulfones that increases the rigidity of the backbone. As a result, sPSScl9 incubated in the presence of V(V) shows unchanged ion exchange capacity and proton conductivity, and a 10× reduction of vanadium permeability with respect to untreated membranes.
File in questo prodotto:
File Dimensione Formato  
M.Gigli (2021 - Sust. Materials & Technologies) - Crosslinked sulfonated poly(phenylene sulfide sulfone) membranes for vanadium redox flow batteries.pdf

non disponibili

Tipologia: Versione dell'editore
Licenza: Accesso chiuso-personale
Dimensione 1.12 MB
Formato Adobe PDF
1.12 MB Adobe PDF   Visualizza/Apri

I documenti in ARCA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10278/3744830
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 12
  • ???jsp.display-item.citation.isi??? 11
social impact