In order to improve the photocatalytic response of TiO2 to UV and visible light for hydrogen photoproduction, low cost M/TiO2 semiconductor catalysts were prepared by the impregnation method of five different first row transition metals (M = Fe, Co, Ni, Cu or Zn) on a commercial titania support. The maximum hydrogen production efficiency was achieved for the Cu/TiO2 photocatalyst, with ∼5000 and ∼220 μmol h−1 g−1 H2 production rates for UV and visible irradiation, respectively. Ni/TiO2 and Co/TiO2 also showed a significant photocatalytic activity when UV light was used. The best performing catalyst, Cu/TiO2, was characterized by TEM and XPS measurements. The data showed that Cu was highly dispersed over the TiO2 support and the copper species existed as both reduced Cu0/Cu+ and oxidized Cu2+ on TiO2. Besides, during the hydrogen production reaction, the reduced Cu was partially oxidized to Cu2+ by the transfer of photogenerated holes under UV or visible light irradiation. With UV and visible lamps, the H2 production rates were higher than those obtained with non-impregnated TiO2 by factors of 16 and 3, respectively. These results demonstrated that a Cu/TiO2 photocatalyst could be considered a promising low-cost alternative to the well-known Pt/TiO2 system for hydrogen production, making the Cu-based catalyst an ideal cost-effective candidate for this reaction.

In order to improve the photocatalytic response of TiO2 to UV and visible light for hydrogen photoproduction, low cost M/TiO2 semiconductor catalysts were prepared by the impregnation method of five different first row transition metals (M = Fe, Co, Ni, Cu or Zn) on a commercial titania support. The maximum hydrogen production efficiency was achieved for the Cu/TiO2 photocatalyst, with similar to 5000 and similar to 220 mu mol h(-1) g(-1) H-2 production rates for UV and visible irradiation, respectively. Ni/TiO2 and Co/TiO2 also showed a significant photocatalytic activity when UV light was used. The best performing catalyst, Cu/TiO2, was characterized by TEM and XPS measurements. The data showed that Cu was highly dispersed over the TiO2 support and the copper species existed as both reduced Cu-0/Cu+ and oxidized Cu2+ on TiO2. Besides, during the hydrogen production reaction, the reduced Cu was partially oxidized to Cu2+ by the transfer of photogenerated holes under UV or visible light irradiation. With UV and visible lamps, the H-2 production rates were higher than those obtained with non-impregnated TiO2 by factors of 16 and 3, respectively. These results demonstrated that a Cu/TiO2 photocatalyst could be considered a promising low-cost alternative to the well-known Pt/TiO2 system for hydrogen production, making the Cu-based catalyst an ideal cost-effective candidate for this reaction.

M/TiO2 (M = Fe, Co, Ni, Cu, Zn) catalysts for photocatalytic hydrogen production under UV and visible light irradiation

E. Moretti
2021-01-01

Abstract

In order to improve the photocatalytic response of TiO2 to UV and visible light for hydrogen photoproduction, low cost M/TiO2 semiconductor catalysts were prepared by the impregnation method of five different first row transition metals (M = Fe, Co, Ni, Cu or Zn) on a commercial titania support. The maximum hydrogen production efficiency was achieved for the Cu/TiO2 photocatalyst, with similar to 5000 and similar to 220 mu mol h(-1) g(-1) H-2 production rates for UV and visible irradiation, respectively. Ni/TiO2 and Co/TiO2 also showed a significant photocatalytic activity when UV light was used. The best performing catalyst, Cu/TiO2, was characterized by TEM and XPS measurements. The data showed that Cu was highly dispersed over the TiO2 support and the copper species existed as both reduced Cu-0/Cu+ and oxidized Cu2+ on TiO2. Besides, during the hydrogen production reaction, the reduced Cu was partially oxidized to Cu2+ by the transfer of photogenerated holes under UV or visible light irradiation. With UV and visible lamps, the H-2 production rates were higher than those obtained with non-impregnated TiO2 by factors of 16 and 3, respectively. These results demonstrated that a Cu/TiO2 photocatalyst could be considered a promising low-cost alternative to the well-known Pt/TiO2 system for hydrogen production, making the Cu-based catalyst an ideal cost-effective candidate for this reaction.
2021
8
File in questo prodotto:
File Dimensione Formato  
Article published.pdf

non disponibili

Tipologia: Documento in Post-print
Licenza: Accesso chiuso-personale
Dimensione 2.77 MB
Formato Adobe PDF
2.77 MB Adobe PDF   Visualizza/Apri

I documenti in ARCA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10278/3741573
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 21
  • ???jsp.display-item.citation.isi??? 19
social impact