Studies of structural, magnetic and dielectric properties of X-type Barium Zinc hexaferrite Ba2Zn2Fe28O46 powder prepared by combustion treatment method using ginger root extract as a green reducing agent

Various quantities of ginger (Zingiber officinale) root extract were used to prepare X-type Barium–Zinc hexaferrite with the chemical composition Ba2Zn2Fe28O46. The powders were prepared using a combustion treatment method, being pre-heated at 550 °C for 4 h with the ginger as a fuel, followed by final heating to 900 °C for 5 h and natural cooling to room temperature to obtain Ba2Zn2Fe28O46 hexagonal ferrite powder. The phase composition of heated powder samples was investigated by X-ray diffraction (XRD), indicating the formation of a mixture of X-type and hematite (α-Fe2O3). Up to 82.6%, X-ferrite was formed at 900 °C with 52.5 g of ginger root extract. Dielectric analysis of the prepared samples shows the frequency-dependent phenomena. All samples were hard magnets, with coercivity values (HC) between 262.2 and 318.3 kA m−1, and squareness ratios > 0.5. The sample prepared with 52.5 g ginger root extract possesses the highest value of saturation magnetisation (MS = 33.87 Am2 kg−1) in comparison with the other prepared samples. Therefore, ginger was shown to be a useful natural plant extract as a reducing fuel for the low-temperature synthesis of X-ferrites. The sample prepared with 35 g ginger root extract shows a broad loss tangent resonance peak between 10 kHz and 100 kHz, while other samples show loss tangent resonance peaks between 300 kHz and 2 MHz frequency range.