This work presents some applications of ZrO2 supported over SBA-15 silica as promoter of sulfated zirconia and as support from CuO/CeO 2 catalytic system for preferential oxidation of CO to CO2 in hydrogen rich streams, used as feed for proton exchange membrane fuel cells (PEMFC). Different amounts of ZrO2, from 10 to 30 wt.% were incorporated. These prepared materials were characterized by powder XRD, adsorption-desorption of N2 at 77 K, transmission and scanning electron microscopy (TEM and SEM) and X-rays photoelectron spectroscopy (XPS). The acidity was studied by thermo-programmed desorption of ammonia (NH 3-TPD). These materials were tested, after treatment with H 2SO4, by 2-propanol dehydration and 1-butene isomerization catalytic tests. The samples were found quite good catalyst with strong acid sites, the sample with 20 wt.% of ZrO2 being the better performing sample. Finally this material was successfully used as support for a CuO/CeO2 system, with 6 wt.% of Cu and 20 wt.% of Ce. The resulting catalyst was tested in the preferential oxidation of CO (CO-PROX) attaining conversions close to 100% and high selectivity to CO2.

Preparation, characterization and catalytic applications of ZrO2 supported on low cost SBA-15

MORETTI, Elisa;LENARDA, Maurizio;
2011-01-01

Abstract

This work presents some applications of ZrO2 supported over SBA-15 silica as promoter of sulfated zirconia and as support from CuO/CeO 2 catalytic system for preferential oxidation of CO to CO2 in hydrogen rich streams, used as feed for proton exchange membrane fuel cells (PEMFC). Different amounts of ZrO2, from 10 to 30 wt.% were incorporated. These prepared materials were characterized by powder XRD, adsorption-desorption of N2 at 77 K, transmission and scanning electron microscopy (TEM and SEM) and X-rays photoelectron spectroscopy (XPS). The acidity was studied by thermo-programmed desorption of ammonia (NH 3-TPD). These materials were tested, after treatment with H 2SO4, by 2-propanol dehydration and 1-butene isomerization catalytic tests. The samples were found quite good catalyst with strong acid sites, the sample with 20 wt.% of ZrO2 being the better performing sample. Finally this material was successfully used as support for a CuO/CeO2 system, with 6 wt.% of Cu and 20 wt.% of Ce. The resulting catalyst was tested in the preferential oxidation of CO (CO-PROX) attaining conversions close to 100% and high selectivity to CO2.
2011
17
File in questo prodotto:
File Dimensione Formato  
Article published.pdf

accesso aperto

Descrizione: Articolo principale
Tipologia: Documento in Post-print
Licenza: Accesso chiuso-personale
Dimensione 1.07 MB
Formato Adobe PDF
1.07 MB Adobe PDF Visualizza/Apri

I documenti in ARCA sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10278/24424
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 11
  • ???jsp.display-item.citation.isi??? 8
social impact